Bayblend® T85 XUV
(PC+ABS) blend; Vicat/B 120 temperature = 130 °C; UV-stabilized and customized colored; good injection molding processing behaviour (easy flowing); excellent long-term ageing behaviour under humid conditions and painting performance; improved chemical resistance; low VOC emissions and odour; density varies with color
- Brand
- Bayblend
- Available in
- Europe Middle-East and Africa, Asia Pacific, Latin America, North America
Typical values
| Property | Value | Unit | Test method | Condition |
|---|---|---|---|---|
| Thermal properties | ||||
| Temperature of Deflection under Load (HDT) | 123 | °C | ISO 75-1,-2 | 0.45 MPa |
| Temperature of Deflection under Load (HDT) | 104 | °C | ISO 75-1,-2 | 1.80 MPa |
| Vicat Softening Temperature | 128 | °C | ISO 306 | 50 N; 50 °C/h |
| Coefficient of Linear Thermal Expansion (CLTE), parallel | 0.7 | 10⁻⁴/K | ISO 11359-1,-2 | 23 to 55 °C |
| Coefficient of Linear Thermal Expansion (CLTE), normal | 0.7 | 10⁻⁴/K | ISO 11359-1,-2 | 23 to 55 °C |
| Rheological properties | ||||
| Melt Viscosity | 230 | Pa·s | b. o. ISO 11443-A | 260 °C; 1,000 s⁻¹ |
| Molding Shrinkage, parallel | 0.55 – 0.75 | % | ISO 294-4 | 60×60×2 mm; 260 °C; MT 80 °C; 500 bar |
| Molding Shrinkage, normal | 0.55 – 0.75 | % | ISO 294-4 | 60×60×2 mm; 260 °C; MT 80 °C; 500 bar |
| Mechanical properties (23 °C; 50 % r. h.) | ||||
| Tensile Modulus | 2400 | MPa | ISO 527-1,-2 | 1 mm/min |
| Yield Stress | 57 | MPa | ISO 527-1,-2 | 50 mm/min |
| Yield Strain | 4.8 | % | ISO 527-1,-2 | 50 mm/min |
| Stress at Break | 56 | MPa | ISO 527-1,-2 | 50 mm/min |
| Nominal Strain at Break | 100 | % | ISO 527-1,-2 | 50 mm/min |
| Izod Notched Impact Strength | 50 | kJ/m² | ISO 180/A | 23 °C |
| Izod Notched Impact Strength | 40 | kJ/m² | ISO 180/A | -30 °C |
| Charpy Notched Impact Strength | 41 | kJ/m² | ISO 179-1/1eA | -30 °C |
| Charpy Notched Impact Strength | 53 | kJ/m² | ISO 179-1/1eA | 23 °C |
| Puncture Impact Behavior - Maximum Force | 5400 | N | ISO 6603-2 | -30 °C |
| Puncture Impact Behavior - Maximum Force | 4400 | N | ISO 6603-2 | 23 °C |
| Puncture Impact Behavior - Puncture Energy | 53 | J | ISO 6603-2 | -30 °C |
| Puncture Impact Behavior - Puncture Energy | 47 | J | ISO 6603-2 | 23 °C |
| Other properties (23 °C) | ||||
| Water Absorption (Saturation Value) | 0.4 | % | ISO 62 | Water at 23 °C |
| Water Absorption (Equilibrium Value) | 0.1 | % | ISO 62 | 23 °C; 50 % r. h. |
| Density | 1115 | kg/m³ | ISO 1183-1 | |
| Electrical properties (23 °C; 50 % r. h.) | ||||
| Relative Permittivity | 2.9 | IEC 60250 | 1 MHz | |
| Relative Permittivity | 3 | IEC 60250 | 100 Hz | |
| Dielectric Dissipation Factor | 100 | 10⁻⁴ | IEC 60250 | 1 MHz |
| Dielectric Dissipation Factor | 20 | 10⁻⁴ | IEC 60250 | 100 Hz |
| Volume Resistivity | 1.00E+16 | Ω·m | IEC 62631-3-1 | |
| Surface Resistivity | 1.00E+16 | Ω | IEC 62631-3-2 | |
| Electric Strength | 35 | kV/mm | IEC 60243-1 | 1 mm |
| Comparative Tracking Index (CTI) | 300 | V | IEC 60112 | Solution A |
| Processing conditions for test specimens | ||||
| Injection Molding - Melt Temperature | 280 | °C | ISO 294-1 | |
| Injection Molding - Mold Temperature | 80 | °C | ISO 294-1 | |
| Injection Molding - Injection Velocity | 240 | mm/s | ISO 294-1 | |