Makrolon® FR6020
Polycarbonate; impact modified; flame retardant; medium viscosity; easy release; UV stabilized; non-reinforced; good hydrolysis resistance
- Brand
- Makrolon
- Available in
- Europe Middle-East and Africa, Asia Pacific, Latin America, North America
Typical values
| Property | Value | Unit | Test method | Condition |
|---|---|---|---|---|
| Thermal properties | ||||
| Temperature of Deflection under Load (HDT) | 114 | °C | ISO 75-1,-2 | 1.80 MPa |
| Temperature of Deflection under Load (HDT) | 127 | °C | ISO 75-1,-2 | 0.45 MPa |
| Vicat Softening Temperature | 136 | °C | ISO 306 | 50 N; 120 °C/h |
| Vicat Softening Temperature | 134 | °C | ISO 306 | 50 N; 50 °C/h |
| Coefficient of Linear Thermal Expansion (CLTE), parallel | 0.49 | 10⁻⁴/K | ISO 11359-1,-2 | 23 to 55 °C |
| Coefficient of Linear Thermal Expansion (CLTE), normal | 0.58 | 10⁻⁴/K | ISO 11359-1,-2 | 23 to 55 °C |
| Burning Behavior | V - 0 | UL 94 | ||
| Burning Behavior | 5VB | UL 94 | 2.0 mm | |
| Burning Behavior | 5VA | UL 94 | 3.0 mm | |
| Relative Temperature Index (RTI, Tensile Impact Strength) | 115 | °C | UL 746B | 1.5 mm |
| Relative Temperature Index (RTI, Tensile Strength) | 125 | °C | UL 746B | 1.5 mm |
| Relative Temperature Index (RTI, Electric Strength) | 125 | °C | UL 746B | 1.5 mm |
| Rheological properties | ||||
| Melt Volume-flow Rate (MVR) | 9 | cm³/10 min | ISO 1133-1 | 300 °C/ 1.2 kg |
| Melt Mass-flow Rate (MFR) | 7.4 – 11.6 | g/10 min | ISO 1133-1 | 300 °C/ 1.2 kg |
| Melt Viscosity | 260 | Pa·s | b.o. ISO 11443-A | 1000 s^-1^/ 300 °C |
| Molding Shrinkage, parallel/normal | 0.6 – 0.8 | % | b.o. ISO 2577 | Value range based on general practical experience |
| Mechanical properties (23 °C; 50 % r. h.) | ||||
| Tensile Modulus | 2380 | MPa | ISO 527-1,-2 | 1 mm/min |
| Yield Stress | 58 | MPa | ISO 527-1,-2 | 50 mm/min |
| Yield Strain | 6 | % | ISO 527-1,-2 | 50 mm/min |
| Stress at Break | 58 | MPa | ISO 527-1,-2 | 50 mm/min |
| Strain at Break | 100 – 999.9 | % | b.o. ISO 527-1,-2 | 50 mm/min |
| Flexural Modulus | 2430 | MPa | ISO 178 | 2 mm/min |
| Flexural Strength | 90 | MPa | ISO 178 | 2 mm/min |
| Flexural Stress at 3.5 % Flexural Strain | 74 | MPa | ISO 178 | 2 mm/min |
| Flexural Strain at Flexural Strength | 6 | % | ISO 178 | 2 mm/min |
| Izod Notched Impact Strength | 62 | kJ/m² | 23 °C | |
| Izod Notched Impact Strength | 26 | kJ/m² | ISO 21305/based on ISO 180/A | -30 °C |
| Izod Notched Impact Strength | 46 | kJ/m² | ISO 21305/based on ISO 180/A | -20 °C |
| Izod Notched Impact Strength | 67 | kJ/m² | ISO 21305/based on ISO 180/A | 23 °C |
| Charpy Notched Impact Strength | 33 | kJ/m² | ISO 21305/based on ISO 179/1eA | -30 °C |
| Charpy Notched Impact Strength | 56 | kJ/m² | ISO 21305/based on ISO 179/1eA | -20 °C |
| Charpy Notched Impact Strength | 69 | kJ/m² | ISO 21305/based on ISO 179/1eA | 23 °C |
| Other properties (23 °C) | ||||
| Density | 1200 | kg/m³ | ISO 1183-1 | |
| Processing conditions for test specimens | ||||
| Injection Molding - Melt Temperature | 280 – 300 | °C | ISO 294 | |
| Injection Molding - Mold Temperature | 80 | °C | ISO 294 | |