Bayblend® FR3015 CTI
(PC-I) blend; flame retardant; Vicat/B 120 temperature = 120 °C; CTI = 600 V; limited available colors
- Brand
- Bayblend
- Available in
- Europe Middle-East and Africa, Asia Pacific, Latin America, North America
Typical values
| Property | Value | Unit | Test method | Condition |
|---|---|---|---|---|
| Thermal properties | ||||
| Temperature of Deflection under Load (HDT) | 114 | °C | ISO 75-1,-2 | 0.45 MPa |
| Temperature of Deflection under Load (HDT) | 101 | °C | ISO 75-1,-2 | 1.80 MPa |
| Vicat Softening Temperature | 118 | °C | ISO 306 | 50 N; 50 °C/h |
| Coefficient of Linear Thermal Expansion (CLTE), parallel | 0.76 | 10⁻⁴/K | ISO 11359-1,-2 | 23 to 55 °C |
| Coefficient of Linear Thermal Expansion (CLTE), normal | 0.78 | 10⁻⁴/K | ISO 11359-1,-2 | 23 to 55 °C |
| Burning Behavior | V-0 | UL 94 | 1.5 mm | |
| Resistance to Heat (Ball Pressure Test, BPT) | 110 | °C | IEC 60695-10-2 | |
| Glow Wire Test (GWFI) | 960 | °C | IEC 60695-2-12 | 3.0 mm |
| Glow Wire Test (GWFI) | 960 | °C | IEC 60695-2-12 | 1.5 mm |
| Glow Wire Test (GWIT) | 775 | °C | IEC 60695-2-13 | 3.0 mm |
| Glow Wire Test (GWIT) | 775 | °C | IEC 60695-2-13 | 1.5 mm |
| Rheological properties | ||||
| Melt Viscosity | 305 | Pa·s | b. o. ISO 11443-A | 260 °C; 1,000 s⁻¹ |
| Molding Shrinkage, parallel | 0.5 – 0.6 | % | ISO 294-4 | 60×60×2 mm; 260 °C; MT 80 °C; 500 bar |
| Molding Shrinkage, normal | 0.5 – 0.6 | % | ISO 294-4 | 60×60×2 mm; 260 °C; MT 80 °C; 500 bar |
| Mechanical properties (23 °C; 50 % r. h.) | ||||
| Tensile Modulus | 2370 | MPa | ISO 527-1,-2 | 1 mm/min |
| Yield Stress | 62 | MPa | ISO 527-1,-2 | 5 mm/min |
| Yield Strain | 5 | % | ISO 527-1,-2 | 5 mm/min |
| Stress at Break | 62 | MPa | ISO 527-1,-2 | 5 mm/min |
| Strain at Break | 118 | % | ISO 527-1,-2 | 5 mm/min |
| Nominal Strain at Break | ≥ 50 | % | ISO 527-1,-2 | 5 mm/min |
| Izod Notched Impact Strength | 19 | kJ/m² | ISO 180/A | -30 °C |
| Izod Notched Impact Strength | 45 | kJ/m² | ISO 180/A | 23 °C |
| Other properties (23 °C) | ||||
| Density | 1180 | kg/m³ | ISO 1183-1 | |
| Electrical properties (23 °C; 50 % r. h.) | ||||
| Volume Resistivity | 4.00E+16 | Ω·m | IEC 62631-3-1 | |
| Surface Resistivity | 5.00E+18 | Ω | IEC 62631-3-2 | |
| Electric Strength | 36 | kV/mm | IEC 60243-1 | 1 mm |
| Comparative Tracking Index (CTI) | 600 | V | IEC 60112 | Solution A |
| Processing conditions for test specimens | ||||
| Injection Molding - Melt Temperature | 260 | °C | ISO 294-1 | |
| Injection Molding - Mold Temperature | 80 | °C | ISO 294-1 | |
| Recommended processing and drying conditions | ||||
| Dry Air Drying Temperature | 80 | °C | ||
| Dry Air Drying Time | 4 | h | ||
| Moisture Content max. (%) | 0 – 0.02 | % | ||
| Melt Temperatures | 240 – 270 | °C | ||
| Standard Melt Temperature | 260 | °C | ||
| Barrel Temperatures | 255 – 265 | °C | Nozzle | |
| Barrel Temperatures | 230 – 240 | °C | Front | |
| Barrel Temperatures | 225 – 235 | °C | Middle | |
| Barrel Temperatures | 220 – 230 | °C | Rear | |
| Mold Temperatures | 60 – 90 | °C | ||
| Hold Pressure (% of Injection Pressure) | 50 – 75 | % | ||
| Plastic Back Pressure (specific) | 50 – 150 | bar | ||
| Peripheral Screw Speed | 0.05 – 0.2 | m/s | ||
| Shot-to-Cylinder Size | 30 – 70 | % | ||
| Vent Depth | 0.025 – 0.075 | mm | ||