Makrolon® GF9415 RE25 CQ
Polycarbonate; 10 % glass fiber reinforced; flame retardant; MVR (300 °C/1.2 kg) 6.0 cm³/10 min; V-0 at 1.5 mm (UL 94); 5VA at 3.0 mm (UL 94); high viscosity; easy release; available in opaque colors only
- Brand
- Makrolon
- Available in
- Europe Middle-East and Africa, Asia Pacific, Latin America, North America
Typical values
| Property | Value | Unit | Test method | Condition |
|---|---|---|---|---|
| Thermal properties | ||||
| Temperature of Deflection under Load (HDT) | 137 | °C | ISO 75-1,-2 | 1.80 MPa |
| Temperature of Deflection under Load (HDT) | 145 | °C | ISO 75-1,-2 | 0.45 MPa |
| Vicat Softening Temperature | 145 | °C | ISO 306 | 50 N; 50 °C/h |
| Coefficient of Linear Thermal Expansion (CLTE), parallel | 0.4 | 10⁻⁴/K | ISO 11359-1,-2 | 23 to 55 °C |
| Coefficient of Linear Thermal Expansion (CLTE), normal | 0.65 | 10⁻⁴/K | ISO 11359-1,-2 | 23 to 55 °C |
| Burning Behavior | V-2 | UL 94 | 0.75 mm | |
| Burning Behavior | V-0 | UL 94 | 1.5 mm | |
| Burning Behavior | 5VA | UL 94 | 3.0 mm | |
| Oxygen Index | 35 | % | ISO 4589-2 | Method A |
| Resistance to Heat (Ball Pressure Test, BPT) | 135 | °C | IEC 60695-10-2 | |
| Relative Temperature Index (RTI, Tensile Impact Strength) | 125 | °C | UL 746B | 1.5 mm |
| Relative Temperature Index (RTI, Tensile Strength) | 125 | °C | UL 746B | 1.5 mm |
| Relative Temperature Index (RTI, Electric Strength) | 125 | °C | UL 746B | 1.5 mm |
| Glow Wire Test (GWFI) | 960 | °C | IEC 60695-2-12 | 0.75 mm |
| Glow Wire Test (GWFI) | 960 | °C | IEC 60695-2-12 | 1.5 mm |
| Glow Wire Test (GWFI) | 960 | °C | IEC 60695-2-12 | 3.0 mm |
| Glow Wire Test (GWIT) | 825 | °C | IEC 60695-2-13 | 0.75 mm |
| Glow Wire Test (GWIT) | 850 | °C | IEC 60695-2-13 | 1.5 mm |
| Glow Wire Test (GWIT) | 850 | °C | IEC 60695-2-13 | 3.0 mm |
| Rheological properties | ||||
| Melt Volume-flow Rate (MVR) | 6 | cm³/10 min | ISO 1133-1 | 300 °C/1.2 kg |
| Melt Viscosity | 330 | Pa·s | b. o. ISO 11443-A | 300 °C; 1,000 s⁻¹ |
| Molding Shrinkage, parallel | 0.65 | % | ISO 294-4 | 60×60×2 mm; 500 bar |
| Molding Shrinkage, normal | 0.45 | % | ISO 294-4 | 60×60×2 mm; 500 bar |
| Mechanical properties (23 °C; 50 % r. h.) | ||||
| Tensile Modulus | 3800 | MPa | ISO 527-1,-2 | 1 mm/min |
| Yield Stress | 62 | MPa | ISO 527-1,-2 | 5 mm/min |
| Yield Strain | 4.8 | % | ISO 527-1,-2 | 5 mm/min |
| Stress at Break | 45 | MPa | ISO 527-1,-2 | 5 mm/min |
| Strain at Break | 15 | % | ISO 527-1,-2 | 5 mm/min |
| Nominal Strain at Break | 10 | % | ISO 527-1,-2 | 5 mm/min |
| Flexural Modulus | 3600 | MPa | ISO 178 | 2 mm/min |
| Flexural Strength | 105 | MPa | ISO 178 | 2 mm/min |
| Flexural Stress at 3.5 % Flexural Strain | 95 | MPa | ISO 178 | 2 mm/min |
| Flexural Strain at Flexural Strength | 5.8 | % | ISO 178 | 2 mm/min |
| Izod Notched Impact Strength | 10 | kJ/m² | ISO 21305/b. o. ISO 180/A | 23 °C; 3 mm |
| Izod Notched Impact Strength | 6 | kJ/m² | ISO 21305/b. o. ISO 180/A | -30 °C; 3 mm |
| Charpy Impact Strength | 150 | kJ/m² | ISO 179-1/1eU | 23 °C |
| Charpy Impact Strength | 130 | kJ/m² | ISO 179-1/1eU | -20 °C |
| Puncture Impact Behavior - Maximum Force | 3900 | N | ISO 6603-2 | 23 °C |
| Puncture Impact Behavior - Maximum Force | 3700 | N | ISO 6603-2 | -30 °C |
| Puncture Impact Behavior - Puncture Energy | 25 | J | ISO 6603-2 | 23 °C |
| Puncture Impact Behavior - Puncture Energy | 15 | J | ISO 6603-2 | -30 °C |
| Other properties (23 °C) | ||||
| Density | 1270 | kg/m³ | ISO 1183-1 | |
| Glass Fiber Content | 10 | % | b.o. ISO 3451-1 | Method A |
| Electrical properties (23 °C; 50 % r. h.) | ||||
| Volume Resistivity | 1.00E+15 | Ω·m | IEC 62631-3-1 | |
| Surface Resistivity | 1.00E+15 | Ω | IEC 62631-3-2 | |
| Electric Strength | 37 | kV/mm | IEC 60243-1 | 1 mm |
| Comparative Tracking Index (CTI) | 175 | V | IEC 60112 | Solution A |
| Processing conditions for test specimens | ||||
| Injection Molding - Melt Temperature | 300 | °C | ISO 294-1 | |
| Injection Molding - Mold Temperature | 110 | °C | ISO 294-1 | |
| Injection Molding - Injection Velocity | 200 | mm/s | ISO 294-1 | |
| Recommended processing and drying conditions | ||||
| Dry Air Drying Temperature | 120 | °C | ||
| Dry Air Drying Time | 2 – 3 | h | ||
| Moisture Content max. (%) | 0 – 0.02 | % | ||
| Melt Temperatures | 280 – 320 | °C | ||
| Standard Melt Temperature | 300 | °C | ||
| Barrel Temperatures | 250 – 260 | °C | Rear | |
| Barrel Temperatures | 270 – 280 | °C | Middle | |
| Barrel Temperatures | 280 – 290 | °C | Front | |
| Barrel Temperatures | 290 – 300 | °C | Nozzle | |
| Mold Temperatures | 80 – 120 | °C | ||
| Hold Pressure (% of Injection Pressure) | 50 – 75 | % | ||
| Plastic Back Pressure (specific) | 50 – 150 | bar | ||
| Peripheral Screw Speed | 0.05 – 0.2 | m/s | ||
| Shot-to-Cylinder Size | 30 – 70 | % | ||
| Vent Depth | 0.025 – 0.075 | mm | ||