Makrolon® FR7087
Polycarbonate; flame retardant; MVR (300 °C/1.2 kg) 12 cm³/10 min; UL 94V-0/2.2 mm and 5VA/3.0 mm; medium viscosity; UV stabilized; easy release; available in transparent and translucent colors
- Brand
- Makrolon
- Available in
- Europe Middle-East and Africa, Latin America, North America, Asia Pacific
Typical values
| Property | Value | Unit | Test method | Condition |
|---|---|---|---|---|
| All attributes | ||||
| Melt Mass-flow Rate (MFR) | 12 | g/10 min | ISO 1133 | 300 °C/1.2 kg |
| Thermal properties | ||||
| Temperature of Deflection under Load (HDT) | 118 | °C | ISO 75-1,-2 | 0.45 MPa |
| Temperature of Deflection under Load (HDT) | 106 | °C | ISO 75-1,-2 | 1.80 MPa |
| Vicat Softening Temperature | 124 | °C | ISO 306 | 50 N; 120 °C/h |
| Vicat Softening Temperature | 123 | °C | ISO 306 | 50 N; 50 °C/h |
| Burning Behavior | V-2 | UL 94 | 1.5 mm | |
| Burning Behavior | V-0 | UL 94 | 2.2 mm | |
| Burning Behavior | 5VA | UL 94 | 3.0 mm | |
| Relative Temperature Index (RTI, Tensile Impact Strength) | 80 | °C | UL 746B | 1.5 mm |
| Relative Temperature Index (RTI, Tensile Strength) | 85 | °C | UL 746B | 1.5 mm |
| Relative Temperature Index (RTI, Electric Strength) | 125 | °C | UL 746B | 1.5 mm |
| Glow Wire Test (GWFI) | 960 | °C | IEC 60695-2-12 | 3.0 mm |
| Glow Wire Test (GWFI) | 960 | °C | IEC 60695-2-12 | 2.2 mm |
| Glow Wire Test (GWFI) | 960 | °C | IEC 60695-2-12 | 1.5 mm |
| Glow Wire Test (GWIT) | 960 | °C | IEC 60695-2-13 | 3.0 mm |
| Glow Wire Test (GWIT) | 930 | °C | IEC 60695-2-13 | 2.2 mm |
| Glow Wire Test (GWIT) | 930 | °C | IEC 60695-2-13 | 1.5 mm |
| Rheological properties | ||||
| Melt Volume-flow Rate (MVR) | 12 | cm³/10 min | ISO 1133-1 | 300 °C/1.2 kg |
| Melt Mass-flow Rate (MFR) | 12 | g/10 min | ISO 1133-1 | 300 °C/1.2 kg |
| Mechanical properties (23 °C; 50 % r. h.) | ||||
| Tensile Modulus | 2500 | MPa | ISO 527-1,-2 | 1 mm/min |
| Yield Stress | 75 | MPa | ISO 527-1,-2 | 50 mm/min |
| Yield Strain | 5 | % | ISO 527-1,-2 | 50 mm/min |
| Stress at Break | 75 | MPa | ISO 527-1,-2 | 50 mm/min |
| Strain at Break | 100 | % | b. o. ISO 527-1,-2 | 50 mm/min |
| Izod Notched Impact Strength | 8 | kJ/m² | ISO 7391/b.o. ISO 180/A | -30 °C; 3 mm |
| Izod Notched Impact Strength | 8 | kJ/m² | ISO 7391/b.o. ISO 180/A | 23 °C; 3 mm |
| Izod Notched Impact Strength | 8 | kJ/m² | 23 °C; 3 mm | |
| Izod Notched Impact Strength | 8 | kJ/m² | -30 °C; 3 mm | |
| Izod Notched Impact Strength | 8 | kJ/m² | ISO 21305/b. o. ISO 180/A | -30 °C; 3 mm |
| Izod Notched Impact Strength | 8 | kJ/m² | ISO 21305/b. o. ISO 180/A | 23 °C; 3 mm |
| Material specific properties | ||||
| Luminous Transmittance | 88 | % | ISO 13468-2 | 3 mm |
| Haze (Clear Transparent Materials) | 0.9 | % | ISO 14782 | 3 mm |
| Processing conditions for test specimens | ||||
| Injection Molding - Melt Temperature | 290 | °C | ISO 294-1 | |
| Injection Molding - Mold Temperature | 80 | °C | ISO 294-1 | |
| Injection Molding - Injection Velocity | 200 | mm/s | ISO 294-1 | |
| Recommended processing and drying conditions | ||||
| Dry Air Drying Temperature | 90 | °C | ||
| Dry Air Drying Time | 4 | h | ||
| Moisture Content max. (%) | 0 – 0.02 | % | ||
| Melt Temperatures | 280 – 320 | °C | ||
| Standard Melt Temperature | 300 | °C | ||
| Barrel Temperatures | 270 – 305 | °C | Nozzle | |
| Barrel Temperatures | 285 – 305 | °C | Front | |
| Barrel Temperatures | 270 – 290 | °C | Middle | |
| Barrel Temperatures | 250 – 270 | °C | Rear | |
| Mold Temperatures | 70 – 110 | °C | ||
| Hold Pressure (% of Injection Pressure) | 50 – 75 | % | ||
| Plastic Back Pressure (specific) | 100 – 200 | bar | ||
| Peripheral Screw Speed | 0.05 – 0.2 | m/s | ||
| Shot-to-Cylinder Size | 30 – 70 | % | ||
| Vent Depth | 0.025 – 0.075 | mm | ||