Polycarbonate; impact modified; flame retardant; MVR (300 °C/1.2 kg) 9.0 cm³/10 min; medium viscosity; easy release; good surface quality
- Brand
- Makrolon
- Available in
- Europe Middle-East and Africa, Asia Pacific, Latin America, North America
Typical values
| Property | Value | Unit | Test method | Condition |
|---|---|---|---|---|
| Thermal properties | ||||
| Temperature of Deflection under Load (HDT) | 121 | °C | ISO 75-1,-2 | 1.80 MPa |
| Temperature of Deflection under Load (HDT) | 136 | °C | ISO 75-1,-2 | 0.45 MPa |
| Vicat Softening Temperature | 142 | °C | ISO 306 | 50 N; 50 °C/h |
| Vicat Softening Temperature | 144 | °C | ISO 306 | 50 N; 120 °C/h |
| Coefficient of Linear Thermal Expansion (CLTE), parallel | 0.7 | 10⁻⁴/K | ISO 11359-1,-2 | 23 to 55 °C |
| Coefficient of Linear Thermal Expansion (CLTE), normal | 0.7 | 10⁻⁴/K | ISO 11359-1,-2 | 23 to 55 °C |
| Burning Behavior | V-0 | UL 94 | 1.0 mm; BK | |
| Burning Behavior | V-1 | UL 94 | 1.2 mm | |
| Burning Behavior | V-0 | UL 94 | 1.5 mm | |
| Resistance to Heat (Ball Pressure Test, BPT) | 134 | °C | IEC 60695-10-2 | |
| Relative Temperature Index (RTI, Tensile Impact Strength) | 105 | °C | UL 746B | 0.75 mm |
| Relative Temperature Index (RTI, Tensile Strength) | 115 | °C | UL 746B | 0.75 mm |
| Relative Temperature Index (RTI, Electric Strength) | 115 | °C | UL 746B | 0.75 mm |
| Glow Wire Test (GWFI) | 850 | °C | IEC 60695-2-12 | 1.0 mm |
| Glow Wire Test (GWFI) | 960 | °C | IEC 60695-2-12 | 1.5 mm |
| Glow Wire Test (GWFI) | 960 | °C | IEC 60695-2-12 | 3.0 mm |
| Glow Wire Test (GWIT) | 875 | °C | IEC 60695-2-13 | 1.0 mm |
| Glow Wire Test (GWIT) | 850 | °C | IEC 60695-2-13 | 1.5 mm |
| Glow Wire Test (GWIT) | 900 | °C | IEC 60695-2-13 | 3.0 mm |
| Rheological properties | ||||
| Melt Volume-flow Rate (MVR) | 9 | cm³/10 min | ISO 1133-1 | 300 °C/1.2 kg |
| Molding Shrinkage, parallel/normal | 0.6 – 0.8 | % | b. o. ISO 2577 | Value range based on general practical experience |
| Mechanical properties (23 °C; 50 % r. h.) | ||||
| Tensile Modulus | 2300 | MPa | ISO 527-1,-2 | 1 mm/min |
| Yield Stress | 62 | MPa | ISO 527-1,-2 | 50 mm/min |
| Yield Strain | 6 | % | ISO 527-1,-2 | 50 mm/min |
| Stress at Break | 66 | MPa | ISO 527-1,-2 | 50 mm/min |
| Strain at Break | 135 | % | ISO 527-1,-2 | 50 mm/min |
| Nominal Strain at Break | ≥ 50 | % | ISO 527-1,-2 | 50 mm/min |
| Flexural Modulus | 2400 | MPa | ISO 178 | 2 mm/min |
| Flexural Strength | 90 | MPa | ISO 178 | 2 mm/min |
| Izod Notched Impact Strength | 60 | kJ/m² | ISO 21305/b. o. ISO 180/A | 23 °C; 3 mm |
| Izod Notched Impact Strength | 50 | kJ/m² | ISO 21305/b. o. ISO 180/A | -10 °C; 3 mm |
| Izod Notched Impact Strength | 15 | kJ/m² | ISO 21305/b. o. ISO 180/A | -30 °C; 3 mm |
| Charpy Notched Impact Strength | 68 | kJ/m² | ISO 21305/b. o. ISO 179-1/1eA | 23 °C; 3 mm |
| Charpy Notched Impact Strength | 50 | kJ/m² | ISO 21305/b. o. ISO 179-1/1eA | -10 °C; 3 mm |
| Charpy Notched Impact Strength | 20 | kJ/m² | ISO 21305/b. o. ISO 179-1/1eA | -30 °C; 3 mm |
| Puncture Impact Behavior - Maximum Force | 5100 | N | ISO 6603-2 | 23 °C |
| Puncture Impact Behavior - Maximum Force | 6100 | N | ISO 6603-2 | -30 °C |
| Puncture Impact Behavior - Puncture Energy | 54 | J | ISO 6603-2 | 23 °C |
| Puncture Impact Behavior - Puncture Energy | 55 | J | ISO 6603-2 | -30 °C |
| Other properties (23 °C) | ||||
| Density | 1200 | kg/m³ | ISO 1183-1 | |
| Electrical properties (23 °C; 50 % r. h.) | ||||
| Volume Resistivity | 9.00E+14 | Ω·m | IEC 62631-3-1 | |
| Surface Resistivity | 4.00E+17 | Ω | IEC 62631-3-2 | |
| Comparative Tracking Index (CTI) | 200 | V | IEC 60112 | Solution A |
| Processing conditions for test specimens | ||||
| Injection Molding - Melt Temperature | 300 | °C | ISO 294-1 | |
| Injection Molding - Mold Temperature | 80 | °C | ISO 294-1 | |
| Injection Molding - Injection Velocity | 200 | mm/s | ISO 294-1 | |
| Recommended processing and drying conditions | ||||
| Dry Air Drying Temperature | 120 | °C | ||
| Dry Air Drying Time | 2 – 3 | h | ||
| Moisture Content max. (%) | 0 – 0.02 | % | ||
| Melt Temperatures | 280 – 320 | °C | ||
| Standard Melt Temperature | 300 | °C | ||
| Barrel Temperatures | 250 – 260 | °C | Rear | |
| Barrel Temperatures | 270 – 280 | °C | Middle | |
| Barrel Temperatures | 280 – 290 | °C | Front | |
| Barrel Temperatures | 290 – 300 | °C | Nozzle | |
| Mold Temperatures | 80 – 120 | °C | ||
| Hold Pressure (% of Injection Pressure) | 50 – 75 | % | ||
| Plastic Back Pressure (specific) | 50 – 150 | bar | ||
| Peripheral Screw Speed | 0.05 – 0.2 | m/s | ||
| Shot-to-Cylinder Size | 30 – 70 | % | ||
| Vent Depth | 0.025 – 0.075 | mm | ||