Bayblend® E3040 W RE25 CQ
(PC+ABS) blend; impact modified; flame retardant; UV stabilized
- Brand
- Bayblend
- Available in
- North America, Asia Pacific, Latin America, Europe Middle-East and Africa
Typical values
| Property | Value | Unit | Test method | Condition |
|---|---|---|---|---|
| Thermal properties | ||||
| Temperature of Deflection under Load (HDT) | 84 | °C | ISO 75-1,-2 | 1.80 MPa |
| Vicat Softening Temperature | 105 | °C | ISO 306 | 50 N; 120 °C/h |
| Burning Behavior | V-2 | UL 94 | 0.75 mm | |
| Rheological properties | ||||
| Melt Volume-flow Rate (MVR) | 27 | cm³/10 min | ISO 1133-1 | 240 °C/5 kg |
| Melt Viscosity | 250 | Pa·s | b. o. ISO 11443-A | 260 °C; 1,000 s⁻¹ |
| Molding Shrinkage, parallel | 0.3 – 0.5 | % | ISO 294-4 | 60×60×2 mm; 500 bar |
| Molding Shrinkage, normal | 0.3 – 0.5 | % | ISO 294-4 | 60×60×2 mm; 500 bar |
| Mechanical properties (23 °C; 50 % r. h.) | ||||
| Tensile Modulus | 2570 | MPa | ISO 527-1,-2 | 1 mm/min |
| Yield Stress | 66 | MPa | ISO 527-1,-2 | 50 mm/min |
| Yield Strain | 4 | % | ISO 527-1,-2 | 50 mm/min |
| Stress at Break | 52 | MPa | ISO 527-1,-2 | 50 mm/min |
| Strain at Break | 68 | % | ISO 527-1,-2 | 50 mm/min |
| Flexural Modulus | 2480 | MPa | ISO 178 | 2 mm/min |
| Flexural Strength | 94 | MPa | ISO 178 | 2 mm/min |
| Izod Notched Impact Strength | 49 | kJ/m² | ISO 180/A | 23 °C |
| Izod Notched Impact Strength | 8 | kJ/m² | ISO 180/A | -30 °C |
| Charpy Impact Strength | 150 | kJ/m² | ISO 179-1/1eU | 23 °C |
| Other properties (23 °C) | ||||
| Density | 1190 | kg/m³ | ISO 1183-1 | |
| Recommended processing and drying conditions | ||||
| Dry Air Drying Temperature | 85 | °C | ||
| Dry Air Drying Time | 4 | h | ||
| Moisture Content max. (%) | 0 – 0.02 | % | ||
| Melt Temperatures | 230 – 300 | °C | ||
| Standard Melt Temperature | 260 | °C | ||
| Barrel Temperatures | 230 – 260 | °C | Rear | |
| Barrel Temperatures | 240 – 270 | °C | Middle | |
| Barrel Temperatures | 250 – 300 | °C | Front | |
| Barrel Temperatures | 250 – 300 | °C | Nozzle | |
| Mold Temperatures | 60 – 90 | °C | ||
| Hold Pressure (% of Injection Pressure) | 50 – 75 | % | ||
| Plastic Back Pressure (specific) | 50 – 150 | bar | ||
| Peripheral Screw Speed | 0.05 – 0.2 | m/s | ||
| Shot-to-Cylinder Size | 30 – 70 | % | ||
| Vent Depth | 0.025 – 0.075 | mm | ||